Concrete structures suffer from the impact of many harmful attacking materials that affect theproperties of the main material in them, which is concrete. These structures are also, exposedto the negative impact of many hostile environments such as soils containing harmful salts andharmful acids. A number of precautions should be considered in order to protect the concreteused in such structures. Adding polymer to concrete components as a percentages weight ofcement is one of the methods for producing polymer-modified concrete, which has lowpermeability, better mechanical properties and is more resistant to the negative effects ofharmful environmental factors. The utilization of polymers could help in protecting structuresand enhancing concrete strength. In this study, concrete mixes were prepared with inclusion ofstyrene butadiene rubber (SBR) polymer at four percentages (0%, 5%, 7% and 10% by cementweight). Co-polymers of butidine with styrene (styrene-butadine rubber (SBR)), are a group oflarge-volume synthetic rubbers. High adhesion occurs between the polymer films that formand cement hydrates. This action gives improves the properties of concrete such as flexuraland compressive strength and gives also a higher durability. The investigation was extended toevaluate the compressive strength of the SBR concrete mixes immersed in three types ofwaters: tap, drainage and ground water, at three different ages. The results showed that SBRpolymer enhanced the compressive strength of concrete significantly. A comparison betweenreduction in strength of concretes immersed in these three types of waters was also presented.Moreover, the presence of SBR polymer led to reduced loss in strength of concrete specimensimmersed in drainage and ground water. A proposed model to determine the compressivestrength of concrete specimens immersed in drainage and ground waters was deduced. Thismodel could be a helpful tool for rapid and easy estimation of the strength of concretespecimens immersed in drainage and ground water at different contents of SBR polymer. Theresults showed the highest improve in compressive strength to be associated with 7% SBRmixes at the three tested ages. The increases in this strength at days 7, 28 and 56 with inclusionof 7% SBR polymer were 112.8%, 113.9% and 116%, respectively, compared to OPC mix.
This research investigates the impact resistace of reinforced high strength concrete slabs with steel meshes (BRC) modified by styrene butadiene rubber (SBR) with different weight ratios of polymer to cement as follows: 3%, 5% and 7%. Reference mix was produced for comparison of results. For all selected mixes, cubes (100×100×100mm) were made for compressive strength test at (365) days. In conducting low-velocity impact test, method of repeated falling mass was used: 1400gm steel ball falling freely from height of 2400mm on reinforced panels of (50×50×800 mm) reinforced with one layer of (BRC). The number of blows causing first crack and final perforation (failure) were calculated, according to the former results, the energy of each case was found. Results showed an improvement in compressive strength of polymer modified high strength concrete (PMHSC) over reference mix; the maximum increase being of it were (3.93%-11.96%) at age of (365) days. There is significant improvement in low-velocity impact resistance of all polymer modified mixes over reference mix. Results illustrated that polymer modified mix of (3%) give the its higher impact resistance than others, the increase of its impact resistance at failure over reference mix was (154.76%) while, for polymer modified mix (5%) it was (30.95%) and it was (14.28%) for polymer modified mix of (7%).
The presented work investigates the effect of addition admixtures (superplasticizer and polymer) to Chopped Worn-Out Tire concrete as a partial replacement of cement weight. Superpasticizer was addition by 4% and polymer (SBR) by 15%. The Chopped Worn-Out Tire (Ch.W.T.) addition to reference concrete with the three proportions as a Partial Replacement Ratio (PRR) of (25,25),(20,30),and (30,20) by volume of (sand and gravel) respectively. Three mixes were selected with above PRR for each type of admixture in additional to three mixes for Ch.W.T. concrete without admixtures and three reference mixes with admixtures without Ch.W.T. Thus, twelve mixes could be used in this investigation. Compressive strength and modulus of elasticity (static and dynamic) were tested. The test results indicated that the use of admixture led to significant improvement in concrete properties in general. Superplasticizer gave best results comparative with polymer, for example at 28 day the compressive strength of superplasticizer Ch.W.T. concrete Csp25,25 was 32.5 MPa, while compressive strength of polymer modified Ch.W.T. concrete CB25,25 was 28 MPa and compressive strength of Ch.W.T. concrete C25,25 was 21.2 MPa.
An experimental investigation as well as nonlinear analysis is carried out in this paper to study the behavior of polymer members (Epoxy & Polyester) under direct tension. The ANSYS model accounts for nonlinear phenomenon, such as, Tension Softening Material (TSM) and Enhanced Multilinear Isotropic Softening (EMIS) models. The polymer specimens are modeled using PLANE82 element – eight node plane element – eight node plane element, which is capable of simulating the failure behavior of polymer material members. The intention of this paper is thereby to discuss the proposed softening models to validate the complete Stress-Strain and Load-Deflection response of prismatic specimens subjected to uniaxial tension. The outcomes from the verifications of both modeling techniques have shown good agreement with the experimental results obtained from literature.
This research work includes production of polymer modified polystyrene concrete and studies the mechanical properties. Several proportions of raw materials were used to produce this type of concrete. This study is intended to improve the mechanical properties of light weight polystyrene concrete using styrene butadiene rubber(SBR) with rate of (5,10,15and20)% of cement weight. Compressive strength, flexural strength, impact strength and dry density tests were made on more than 150 specimen at age of 28 days. The results show that the addition of (SBR) with range of (5-20)%of cement weight is improve the flexural strength with range (3.74-18)%, and improve the impact strength with range (39-163)%. Also the results show that it is possible to produce polystyrene concrete with density (1680,1433 and 1147) kg/m3 replacing light weight Polystyrene aggregate with volume fraction (30,50 and70)%of sand.
In this research, the effect of adding fillings of steel resulting from factory of smithery was studied. The fiber was added with two different percentages to the ordinary and polymer concrete to study their effects on some of the properties of both type of concrete like compressive strength, flexural strength and density. Two different percentages of fiber by volume of concrete (0.5%, 1.0%) were added to concrete mixes. A reference mix was also made. The results showed that adding of fillings of steel with these percentages lead to improvements in both compressive strength and flexural strength of polymer concrete with the increase of its percentage while it's less effect on these properties of ordinary concrete. An improvement in flexural strength appeared more clearly in both type of concrete. Significant increase in density was noted in both types of concrete.
This research includes the study of bending strength for the polymer composite materials. The first of all, the hand lay-up technology is used to prepare slates of the composite materials, epoxy resin was used as matrix for the reinforced materials that consist of artificial powders (aluminum oxide and copper) for reinforcing. The slates made of composite materials for both volume fractions 20% and 40% from the reinforced materials; all these slates were cut into samples with measurement (10x 100 mm) in order to carry out the bending strength test for samples by using cantilever bending test for both volume fractions 20% and 40%. The results and laboratory examinations for these samples shows increase in the bending strength and modulus of elasticity for composite materials when the volume fraction increase from 20% to 40% for reinforced materials, and these values decrease when the samples were immersion in distilled water for (30) days.
The Organo modified and unmodified sodium montmorillonite clay effect on thermal and mechanical properties of the waste low density polyethylene (wLDPE) were studied. Commercialize unmodified (MMT) and Organo-modified clay (OMMT) were added to the wLDPE to prepare wLDPE-clay noncomposites by melt intercalation method. OMMT and MMT were added in a range of 1-5 wt %. Fourier transform infrared spectroscopy (FTIR) used to evaluate polymer structure before and after the fabrication. Thermogravimetric analysis (TGA) and Differential Scanning Calorimetry (DSC) were used to analyse the thermal stability and thermal properties for the wLDPE and fabricated nanocomposites. Tensile mechanical characteristics of the waste specimens before and after nanocompsite fabrication were evaluated. The FTIR exhibited no change in the chemical structure of the wLDPE used after clay addition. Melting temperature and crystallization percentage were increased up to 1 wt% loaded and decreased in with clay content increasing when compared to the original waste matrix. The thermal steadiness of the wLDPE /clay nanocomposites were found enhanced in the case of loading 3 wt% of OMMT. The elastic modulus has improved in the 3% OMMT loaded.
The present research aimed to study the effect of distilled water on impact strength for unsaturated polyester composites reinforced with E-glass fibers with volume fraction 35%, all samples were prepared by using hand lay up technique. Unsaturated polyester resin was used as matrix for the reinforced materials that consist of artificial glass fibers (woven roving) with directional (0,90) and chopped glass fibers with the random direction. The samples were cutting with measurement (60 x 6) mm and the sample thickness dependent on the number of layers of glass fibers. The impact tests are carried out on samples under the influence of normal conditions (laboratory temperature). The results and examinations for these samples shows acceptable improvement in impact strengths of the matrix was observed after addition of glass fibers, to explain the effect of water on impact properties, the samples immersion in water for (50) days. The results show that as the exposure time increased the impact strength of samples increase.