The White Cement Kiln Dust (WCKD) is a byproduct material, formed in cement factory during the operation of cement production. In highway construction, the WCKD can be used in different ways such as stabilizing the subgrade of highway embankment and as mineral filler in Hot Mix Asphalt (HMA); the latter usage will give clean and healthy environment in addition to more economy. In Iraq, there are two common types of fillers, Portland cement and lime stone powder. In this research, WCKD taken from Fallujah cement plant used as mineral filler in addition to two common types. Various percentages , such as 100%WCKD, 50%WCKD + 50%Cement(C) ,100%C , 50%WCKD+50%Limestone (L), and 100% L, were used to prepare asphaltic concrete mixes. In general, five tests were used to evaluate the performance of these mixes. Standard Marshall Test procedure was applied under three different conditions, two of them at two temperatures at 60 OC and 70 OC and in the third one it was used to test samples immersed in water, at room temperature(24 OC), for four days. Indirect Tensile Strength Test (ITST) was used to evaluate conditioning and un-conditioning samples. All test results, when compared with controlled asphalt concrete sample (Sample contained 100% limestone as filler), were acceptable and within the AASHTO and Iraqi Standard Specifications of Roads & Bridges 2003. Stability values, at standard condition test, of samples containing 100% WCKD, 50%WCKD+50%C, and 50%WCKD+50%L are 11.9kN, 13.2kN, and 14.0kN respectively, while for controlled sample was 9.0kN. The Marshall stiffness values showed similar trends, for samples having 100% WCKD, 50%WCKD+50%C, and 50%WCKD+50%L giving 3.22kN/mm, 3.38kN/mm, 3.5kN/mm respectively but for controlled sample was 2.43 kN/mm. Same trends of results gained in ITST .The results showed the beneficial using of WCKD as filler that will conserve the environment and encourage the HMA producers to use this inexpensive material in their works.
Thousands of tons of marble waste can be reused every year in Iraq. Few investigations are made to study the effect of marble as a filler on hot mix asphalt concrete.. This big amount of waste has a bad effect on the environment and needs a lot of money and effort for recycling or disposal. Lime stone dust was used as a control filler. The laboratory tests have been conducted in order to evaluate the properties of each type of filler, which consist of the grain size distribution, the specific gravity (Gs), specific surface area (SA), pore volume(PV), mineral composition, pH and chemical composition.To study the effect of SM on the performance of HMA mixture, several tests were made consist of Marshall stiffness, Indirect tensile strength, Moisture susceptibility and Creep tests. Many conclusions were achieved referring the importance of using Sulaimania Marble waste (SM) in the enhancing most of the properties of HMA concrete.