The presented work investigates the effect of addition admixtures (superplasticizer and polymer) to Chopped Worn-Out Tire concrete as a partial replacement of cement weight. Superpasticizer was addition by 4% and polymer (SBR) by 15%. The Chopped Worn-Out Tire (Ch.W.T.) addition to reference concrete with the three proportions as a Partial Replacement Ratio (PRR) of (25,25),(20,30),and (30,20) by volume of (sand and gravel) respectively. Three mixes were selected with above PRR for each type of admixture in additional to three mixes for Ch.W.T. concrete without admixtures and three reference mixes with admixtures without Ch.W.T. Thus, twelve mixes could be used in this investigation. Compressive strength and modulus of elasticity (static and dynamic) were tested. The test results indicated that the use of admixture led to significant improvement in concrete properties in general. Superplasticizer gave best results comparative with polymer, for example at 28 day the compressive strength of superplasticizer Ch.W.T. concrete Csp25,25 was 32.5 MPa, while compressive strength of polymer modified Ch.W.T. concrete CB25,25 was 28 MPa and compressive strength of Ch.W.T. concrete C25,25 was 21.2 MPa.
In General, original reactive powder concrete (RPC) consists of a superplasticized cement mixture with silica fumes, steel fiber and ground fine sand (150-600 ىm). The main purpose of the present work is to produce and study some mechanical properties of lightweight reactive powder concrete using a superplasticized cement mixture with high reactivity metakaolin (HRM) instead of silica fume, steel fiber (with different ratios ) with ground fine sand (150-600 ىm) and light weight material called (Perlite ) also with different ratios .This investigation was carried out using several tests, these tests were compressive strength, modulus of rupture, modulus of elasticity, density and absorption, and performed for specimens at ages of 3, 7, 28 days, respectively. The tests results were compared with a reference mix. The experimental results shows that , with different ages, (for constant Perlit ratio for 0% to 10% as additional cementtitious materials) addition of 1% steel fiber will improve about (8.3%-10% , 3.2%-11%and 0.25%- 8%) for compressive strength , modulus of rupture, and modulus of elasticity respectively, and increase density, absorption about (0.8%-1.8%,4.5%-8.2%) respectively. Also an increase of steel fiber ratio to 2% will improve about (16.5%-20.3%, 9.0%-17%, and 1.7%-11.5%) for compressive strength , modulus of rupture and modulus of elasticity respectively, and increase density, absorption about (1.7%-2.3% , 7.3%-8.3%) respectively. For same steel fiber ratio about 0% to 2%, increasing Perlite ratio to 2.5% will decrease about (17.3%-18.8%, 9.5%-15.5%, 4.4%-16.6%, and 4.98% - 6.9%) for compressive strength, modulus of rupture, modulus of elasticity and density respectively and increase absorption to about (55.5% - 66.5%). Increasing the ratio to 5% will also make a decrease of about (36%-36.77%, 33.7%-37%, 16.5%- 21.88%and 15.91%-19.74%) for compressive strength, modulus of rupture, modulus of elasticity and density respectively and increase absorption for about (106%- 110.5%) . Increasing the ratio to 10% will also decrease about (45.98%-47.2%, 46.5-54.2%, 30.6%- 35.57%and 19.4%-23.36%) for compressive strength, modulus of rupture, modulus of elasticity and density respectively and increase absorption about(183%- 192.6%). To produce structural lightweight concrete, the tests results show that the optimum steel fiber is 1% by volume and optimum Perlite ratio is 2.5% by weight of cement as additional materials.
Concrete structures suffer from the impact of many harmful attacking materials that affect theproperties of the main material in them, which is concrete. These structures are also, exposedto the negative impact of many hostile environments such as soils containing harmful salts andharmful acids. A number of precautions should be considered in order to protect the concreteused in such structures. Adding polymer to concrete components as a percentages weight ofcement is one of the methods for producing polymer-modified concrete, which has lowpermeability, better mechanical properties and is more resistant to the negative effects ofharmful environmental factors. The utilization of polymers could help in protecting structuresand enhancing concrete strength. In this study, concrete mixes were prepared with inclusion ofstyrene butadiene rubber (SBR) polymer at four percentages (0%, 5%, 7% and 10% by cementweight). Co-polymers of butidine with styrene (styrene-butadine rubber (SBR)), are a group oflarge-volume synthetic rubbers. High adhesion occurs between the polymer films that formand cement hydrates. This action gives improves the properties of concrete such as flexuraland compressive strength and gives also a higher durability. The investigation was extended toevaluate the compressive strength of the SBR concrete mixes immersed in three types ofwaters: tap, drainage and ground water, at three different ages. The results showed that SBRpolymer enhanced the compressive strength of concrete significantly. A comparison betweenreduction in strength of concretes immersed in these three types of waters was also presented.Moreover, the presence of SBR polymer led to reduced loss in strength of concrete specimensimmersed in drainage and ground water. A proposed model to determine the compressivestrength of concrete specimens immersed in drainage and ground waters was deduced. Thismodel could be a helpful tool for rapid and easy estimation of the strength of concretespecimens immersed in drainage and ground water at different contents of SBR polymer. Theresults showed the highest improve in compressive strength to be associated with 7% SBRmixes at the three tested ages. The increases in this strength at days 7, 28 and 56 with inclusionof 7% SBR polymer were 112.8%, 113.9% and 116%, respectively, compared to OPC mix.
This research, an attempt is carried to explain the use of new products of superplasticizers type (Glenium) locally recent period used in normal concrete strength,espeacailly in precast concrete. and the effect of medium hot weather climates on compressive strength of normal concrete made with various percentages of Glenium dosages , and to evaluate the dosages on workability of fresh concrete. Concrete mixes with two types containing of Glenium, G51 and G21. and different dosages of Gelnium, namely 0.8 and 1.2 liter per 100 kg of cement and reduction in water quantity about 25% Five mixes are made with 90 specimens, each mix contains 18 cubes ,half of specimens are cured by moist curing in normal condition, the other half of specimens are exposed to temperatures of 40oC.which is transferred to moist medium of hot water. The properties which are covered in this work consist of workability which represented by slump test, and strength represented by compressive strength and ultrasonic pulse velocity(UPV) tests. It is obtained that using the two types of Gelnium will improve the slump about (157% to 183%) compared with reference mix .The concrete cured at medium hot weather condition, show improves in compressive about (19.2 to38.12%) at 3 days age. The use Glenium type 51 is to be more suitable for normal concrete works in medium hot weather .
Some mechanical properties of mortar (compressive strength and hardness) with sawdust replacement of sand were investigated. Cubes of 50 mm × 50 mm were prepared, the compressive strength tests were done for a replacement levels ranging (5, 10, 15, 25, 50, 75) % by volume a reference mix were also prepared for comparison this test was done after 7, 14, and 28 days while hardness test were done after 28 day for a replacement levels (0, 5, 10, 15, 25) % by volume. Result showed that the compressive strength of the specimen were decreased with higher sawdust content, hardness values were decreased slightly in the replacement levels 0, 5, 10 % while the values began to decrease noticeably in the replacement levels 15 and 25 % the hardness values were (59, 57.5, 56, 47.77 , 45.2) N/mm2 respectively A cost analysis was done, this analysis was based on a unit of mortar (1.0 m3) made from conventional materials and a modified concrete made by substituting materials with sand using sawdust
Scientists have recently started looking for new ecologically friendly and sustainable materials. Construction materials are among the numerous widely employed materials, and it is normally acknowledged that they have an apparent detrimental influence on the environment. Thus, the contribution of this paper is to describe the palm frond natural fibers' effect on concrete's mechanical characteristics. Since concrete is a brittle material, the goal of this research is to increase the tensile strength of concrete by using organic fibers (palm frond fibers), a waste product. In order to determine the ideal percentage of fibers, the following percentages were tested: 0.25, 0.5, 0.75, and 1% by volume of concrete. On dry density, compressive strength, and tensile strength, the impacts of fibers were investigated. The density of concrete decreased with increasing fiber ratios. The compressive strength slightly decreased, while the splitting strength significantly improved. According to the results, the best amount of palm frond fibers that can be add to concrete is 0.75% by volume.
The purpose of this paper is to developing a mathematical relationship between the Ultrasonic Pulse Velocity (UPV) and the compressive strength for concrete specimens subjected to different amounts of exposure of sulfate attack. The experimental data were collected from a research work by the author using concrete subjected to sulfate exposure and form a literature used an extensive concrete work without sulfate exposure. The sulfate exposures studied were 0%, 3%, and 6% of fine aggregate. It is found that with the same amount of sulfate exposure a clear relationship curve can be drawn to describe the UPV and compressive strength. This paper proposes the UPV-strength mathematical expression suitable for prediction of the concrete strengths when subjected to sulfate attack.
During the last years, several researches have been studying the final disposal of tyres wastes, due to the great volume generated worldwide, as well as the difficulty for discarding the disposal sites which become a serious environmental problem. In spite of this, recycling appears as the best solution for disposing tyres residues, due to its economical and ecological advantages. This research carried out to assess the feasibility of using crumb rubber (the product of shredding used rubber tyres) as a partial sand replacement in foamed concrete, and investigates the effect of it on some properties of foamed concrete such as, density, water absorption, compressive strength, tensile strength, flexural strength and impact resistance. Crumb rubber of tyres ranging from (0.7 to 5mm) in size was used in this research. Three proportioned mixes were designed in this research, have the same cement content, water-cement ratio, and foam content. The first mix represents a typical reference formulation of foamed concrete without crumb rubber (FC). In the others mixes (FCR-1 and FCR-2), respectively, 20 and 30% of volume of sand were replaced by crumb tyres rubber waste. Tests carried out to assess the behaviour of final product. The results obtained were demonstrated decreasing in foamed concrete strength (compressive, tensile, flexural, and impact) with the increasing of crumb tyres rubber content in the mixture and rubberized foamed concrete specimens (FCR-1 and FCR-2) show a cohesive behaviour than the specimens of reference mix (FC), especially in tensile strength. Comparing with the reference mix (FC), at an age of (28 days), the decreasing of compressive strength was (20.85%) for (FCR-1) and it for (FCR-2) was (37.76%).
The presented work investigates the effect of addition admixture (cement kiln dust) to concrete as a partial replacement of cement weight. Cement kiln dust was added by (10,30,50)% of cement weight.Four mixes were selected, three of them contain cement kiln dust (CKD) and one reference mix without any admixture for ages (7,28,90) days. Compressive strength ,flexural strength, ultra-sound velocity (UPV), slump, splitting tensile strength and static modulus of elasticity were tested.The test results indicated that the use of (CKD) led to significant decreasing in concrete strength in general and this decreasing increases with the increasing of (CKD), for example at 28 day the compressive strength of reference concrete (A) was 35 MPa, while the compressive strength of (B,C,D) contain (10,30,50)%CKD were (28,25,22) MPa respectively.
This research investigates the impact resistace of reinforced high strength concrete slabs with steel meshes (BRC) modified by styrene butadiene rubber (SBR) with different weight ratios of polymer to cement as follows: 3%, 5% and 7%. Reference mix was produced for comparison of results. For all selected mixes, cubes (100×100×100mm) were made for compressive strength test at (365) days. In conducting low-velocity impact test, method of repeated falling mass was used: 1400gm steel ball falling freely from height of 2400mm on reinforced panels of (50×50×800 mm) reinforced with one layer of (BRC). The number of blows causing first crack and final perforation (failure) were calculated, according to the former results, the energy of each case was found. Results showed an improvement in compressive strength of polymer modified high strength concrete (PMHSC) over reference mix; the maximum increase being of it were (3.93%-11.96%) at age of (365) days. There is significant improvement in low-velocity impact resistance of all polymer modified mixes over reference mix. Results illustrated that polymer modified mix of (3%) give the its higher impact resistance than others, the increase of its impact resistance at failure over reference mix was (154.76%) while, for polymer modified mix (5%) it was (30.95%) and it was (14.28%) for polymer modified mix of (7%).
In this research, the effect of adding fillings of steel resulting from factory of smithery was studied. The fiber was added with two different percentages to the ordinary and polymer concrete to study their effects on some of the properties of both type of concrete like compressive strength, flexural strength and density. Two different percentages of fiber by volume of concrete (0.5%, 1.0%) were added to concrete mixes. A reference mix was also made. The results showed that adding of fillings of steel with these percentages lead to improvements in both compressive strength and flexural strength of polymer concrete with the increase of its percentage while it's less effect on these properties of ordinary concrete. An improvement in flexural strength appeared more clearly in both type of concrete. Significant increase in density was noted in both types of concrete.
In this study the effect of sodium hydroxide on the strength of clayey soil-cement mixtures was investigated. Clay soils from three various locations of Kirkuk governorate namely Erbil, Laylan and Hawija check points were used. The effect of cement content, curing age, curing temperature and concentration of sodium hydroxide on the strength of soil-cement mixtures were investigated, through carrying out unconfined compressive strength, Triaxial compression and C.B.R tests. It was found that the use of sodium hydroxide markedly improves the strength of soil-cement mixtures. The addition of about 1% of sodium hydroxide by weight of soil could reduce about 5% of cement content by weight of soil required to stabilize the soils effectively.
This study aims to improve different properties of sustainable self-compacting concrete SCC containing treated and modified polyethylene terephthalate PET fibers. For this purpose, gamma ray surface treatment and geometric modification were utilized for the used PET fibers. Concrete fresh properties include slump flow, T500mm, L-box and sieve segregation while mechanical properties include compressive, split tensile strength, flexural strength, static modulus of elasticity and impact strength. Further, physical properties and related durability properties comprise dry density, ultrasonic pulse velocity, porosity and water absorption. The results obtained demonstrated that the treatment and the modification used for the PET fibers slightly reduced the fresh properties of produced sustainable SCC (slump flow, T500 mm, L-Box and sieve segregation). However, they were within the limits of the SCC specification as reported in EFNERC guidelines. Further, concrete hardened properties in terms of compressive strength, splitting tensile strength, flexural strength, modulus of elasticity, impact strength, ultrasonic pulse velocity, decrease in the dry density, decrease in porosity and water absorption increased significantly.
This investigation was conducted to assess the efficacy of some environmental conditions of soil specimens stabilized with optimum waste lime content 6%. These conditions are represented by cycles of (wetting-drying-freezing), (wetting-freezing-drying), (drying-wetting-freezing), (drying-freezing-wetting), (freezing-wetting-drying) and (freezing-drying-wetting). The soil specimens were subjected to these conditions, the durability of these specimens is study by knowledge the change in unconfined compressive strength, volume change and loss in weight. The results indicated that the unconfined compressive strength decreases with cycles for all conditions, but for different percentages according to the type condition. Where the condition more effect that starting freezing-drying-wetting. Also the results show that the specimens subjected to cycles of (freezing-drying-wetting) and (wetting-freezing-drying) destroyed at the end of eight cycle, but the specimens were subjected to other conditions destroyed at the end of tenth cycle. The results show that the maximum loss in weight for specimens subjected to cycles starting wetting-freezing-drying, and the maximum value of volume change for cycles starting freezing-drying-wetting. Finally these condition are regarded very severe conditions and effect on durability of soil stabilized.
Problematic soils, especially clayey soil, are problematic for engineering projects in their natural state because of clay's swell-shrinkage phenomenon. Numerous methods and stabilizer materials have been used to enhance clay's geotechnical properties and make them appropriate for construction. One of the significant methods of stabilization of problematic soil is using waste materials like waste glass, waste stone, waste plastic, etc. Due to the waste stone's consistency reducing water content and increasing the soil's strength, it has been employed in many civil engineering studies. Waste stone is available in various forms, including waste stone powder (WSP). WSP is produced by blasting tunnels or cutting huge stone blocks. Hence, the main aim of this study is to review the influence of WSP on improving the geotechnical properties of problematic soils treated with WSP, for this purpose, the treated problematic soils with various percentages of WSP are compared with natural soils. This study evaluates physical properties (i.e., Index properties, linear shrinkage/swelling, optimum moisture content, and maximum dry density) and mechanical properties (i.e., unconfined compressive strength and California bearing ratio). Also, the effect of WSP on decreasing the thickness of pavement layers was reviewed
This study aims to investigate the durability properties and microstructural changes of self-compacting concrete (SCC) incorporating waste polyethylene terephthalate (PET) as fibers and as fine aggregate replacement. This is after exposed to saline environment (Alkalies, Sulphates, and Chlorides). PET effect into two forms was also evaluated for routine rheological properties of SCC and mechanical strength before and after exposure to sulphate salt. Five proportions of each form of PET incorporation in SCC mixtures were utilized. The volume fractions considered for PET as fibers were (0.25, 0.5, 0.75, 1.0, and 1.25)% by volume, with aspect ratio of 28%, and (2, 4, 6, 8, and 10)% by volume for fine aggregate replacements. Results indicated that the inclusion of PET adversely affected fresh propertis especially high proportions of PET as fine aggregate. Alkali silica reaction (ASR) outcomes illustrated an enhancement in the mix containing PET fibers, while fine-PET mix was slightly enhanced. Magnesium sulphate reduced mass and compressive strength of all mixes in percentages ranging from (0.18-0.90) % for mass loss and from (0.47-55.13) % for compressive strength loss. Ultrasonic pulse velocity (UPV) and dynamic modulus of elasticity (Ed) increased due to the sulphate impact except for M0.5 and M10 which decreased in both tests. Chloride's theoretical and modelled results illustrated higher diffusion coefficients and lower surface chloride content of fiber-PET mixes as compared to fine-PET mixes. The predicted SCC cover depths for fiber-PET mixes were lower than those predicted for fine-PET mixes for 20 and 50 years of service life design.
This investigation provides experimental results and nonlinear analysis by using finite element model of thick hollow core slab made from recycled lightweight material. Four hollow core slabs specimens were cast and tested in this investigation with dimensions (1200mm length, 450mm width and 250mm thickness). The crushed clay brick was used as a coarse aggregate instead of gravel. The iron powder waste and silica fume were used in order to increase the compressive strength of concrete. The techniques reduction hollow length and use shear reinforcement were used to improve shear strength and avoid shear failure. The specimens were tested by applying two-line load up to failure. The experimental results were showed these techniques were resisted the shear failure significantly and works to change failure mode from shear to flexural failure. Finite element computer software program (ANSYS) was used to analysis hollow core slabs specimens and compare the experimental results with the theoretical results. Good agreement have been obtained between experimental and numerical results.
The impact resistances of concrete slabs have a different volume fraction replacement of waste plastic aggregate has been examined in this study as a fine aggregate as: 0% (reference), 10%, 20% and 30%. These tests include the splitting tensile, density, compressive strength. Also, the (ultrasonic pulse velocity tests) was carried out. Repeated falling mass was used in order to carry out the low-velocity impact test in which a 1300 gm steel ball was utilized. From a height of 2400mm, the ball falls freely on concrete panels of (500×500×50 mm) with a network of waste plastic aggregate. As per the results, a prominent development was seen in the mechanical properties for mixes involving polyethylene aggregate up to 20% as compared to the reference mix. A significant development was seen in low-velocity impact resistance of all mixes involving waste plastic fine aggregate as compared to reference mix. As per the results, the greater impact resistance at failure is offered by the mix with (20%) waste plastic aggregate by volume of sand than others. The reference mix increased by (712.5%).
The construction of pavement layers on subgrade soil with good characteristics decreases the thickness of these layers, which in turn lowers the cost of building and maintaining roadways. However, it is impossible to avoid constructing pavements on unsuitable subgrade due to a number of limitations. Using conventional additives like lime and cement to improve subgrade properties results in additional costs. As a result, utilizing by-products (cement kiln dust and reclaimed asphalt pavement) in this field has benefits for the environment, economy, and technology. Large amounts of cement kiln dust (CKD), a by-product material, are produced in Portland cement factories. On the other hand, large amounts of reclaimed asphalt pavement (RAP) are accumulated as a result of the rehabilitation of old roads. This paper discusses using CKD and RAP to improve the characteristics of poor subgrade layers by conducting a series of Unconfined Compressive Strength (UCS) and California Bearing Ratio (CBR) tests on samples of natural soil and soil stabilized with different percentages of CKD and RAP with different curing times to investigate their impacts on soil properties. The curing was carried out by wrapping the stabilized samples with several layers of nylon and then placing them in plastic bags at room temperature. The compaction results illustrated that the addition of CKD increases OMC and decreases MDD, in contrast to RAP, which decreases OMC and increases MDD. The addition of CKD and RAP led to a significant and unexpected increase in the CBR values. The results show that the soaked and unsoaked CBR values improve from 3.4% and 12.1% for natural soil to 220.1% and 211%, respectively, after adding 20% CKD and curing the samples for 28 days. Also, the addition of 25% RAP to soil-20% CKD blend increased the soaked and unsoaked CBR values to 251% and 215%, respectively. All the additions resulted in a significant reduction in swelling.
This research work includes production of polymer modified polystyrene concrete and studies the mechanical properties. Several proportions of raw materials were used to produce this type of concrete. This study is intended to improve the mechanical properties of light weight polystyrene concrete using styrene butadiene rubber(SBR) with rate of (5,10,15and20)% of cement weight. Compressive strength, flexural strength, impact strength and dry density tests were made on more than 150 specimen at age of 28 days. The results show that the addition of (SBR) with range of (5-20)%of cement weight is improve the flexural strength with range (3.74-18)%, and improve the impact strength with range (39-163)%. Also the results show that it is possible to produce polystyrene concrete with density (1680,1433 and 1147) kg/m3 replacing light weight Polystyrene aggregate with volume fraction (30,50 and70)%of sand.
Ten simply supported deep beams with high strength concrete (C55 MPa) have been casted and subjected to a four-point loading test. Different parameters were examined for their influence on specimen behavior. These parameters were the shear span to overall depth ratio (a/h), the overall depth of deep beams (h), and additional anchorage length beyond the centerline of support (la). The experimental results show that the beam capacity decreases as the shear span to the overall depth ratio increases, and the overall depth and embedment length decrease. The major effect of anchorage length on the shear strength is studied. Different failure modes were observed which do not match strut-and-tie failure modes. The shear compression and anchorage failures were con-trolled in the high compressive concrete deep beams due to bottom steel yielding. Finally, the ex-perimental test results are compared with predictions of the strut-and-tie method according to the ACI 318-14 and a good agreement was found.
Portland cement consists of major oxides which include CaO, SiO2, Al2O3 and Fe2O3 as well as minor oxides which include: SO3 , MgO, Na2O and K2O, the last two oxides are called alkalis oxides. The research aims to study the effect of alkalis oxide ( Na2O+ K2O) on some physical properties of ordinary Portland Iraqi cement (type I) and sulfate - resisting Portland Iraqi cement (type V) provided from (Taslooja Factory) are used in the experimental work. The physical properties of the two types above , which are used in the experimental work, are initial and final setting time, soundness and compressive strength at (3, 7 and 28)days. The results show that the values of physical properties of type I and type V increase when the alkalis percentage increases up to 0.6 percent, while the value of the physical properties of the two types of cement mentioned above begins to reduce even when the percentage of alkalis still increases. Through the use of the ordinary Portland cement (type I) and the sulfate resisting Portland cement (type V), it is found that there is a little difference in the value of the physical properties.
The porous Titanium is characterized by high permeability which can assure the ingrowth of bone tissues, and consequently results in a good bonding between the metallic implant and the bone. In this work, Silicon element was added to the Commercially Pure Titanium at different weight percent of (2, 4, 6, 8 and 10) to investigate its effect on the porosity percentage, mechanical properties of the resulted samples. XRD analysis stated that at (Si) content lower than (2 wt%) the alloy is single phase (α- Ti alloy), as the Silicon content increased, in addition to (αphase), (Ti5Si3) intermetallic compound developed in the alloy. Porosity measurement results showed that the porosity percentage increases with the increase in Silicon content. Wear results stated that the wear rate increases with the increase in silicon content due to the increase in porosity percentage while the hardness results stated that there is no significant effect for Ti5Si3 intermetallic compound on improving the hardness of the samples. This is attributed to its low percent and the major effect of porosity on hardness which declined the effect of Ti5Si3 by reducing the hardness of the alloy compared with the master sample. The obtained results of the (yield strength, ultimate compressive strength and Young’s modulus) were within the values that match bone’s properties. This means these materials are suitable for biomedical application