The White Cement Kiln Dust (WCKD) is a byproduct material, formed in cement factory during the operation of cement production. In highway construction, the WCKD can be used in different ways such as stabilizing the subgrade of highway embankment and as mineral filler in Hot Mix Asphalt (HMA); the latter usage will give clean and healthy environment in addition to more economy. In Iraq, there are two common types of fillers, Portland cement and lime stone powder. In this research, WCKD taken from Fallujah cement plant used as mineral filler in addition to two common types. Various percentages , such as 100%WCKD, 50%WCKD + 50%Cement(C) ,100%C , 50%WCKD+50%Limestone (L), and 100% L, were used to prepare asphaltic concrete mixes. In general, five tests were used to evaluate the performance of these mixes. Standard Marshall Test procedure was applied under three different conditions, two of them at two temperatures at 60 OC and 70 OC and in the third one it was used to test samples immersed in water, at room temperature(24 OC), for four days. Indirect Tensile Strength Test (ITST) was used to evaluate conditioning and un-conditioning samples. All test results, when compared with controlled asphalt concrete sample (Sample contained 100% limestone as filler), were acceptable and within the AASHTO and Iraqi Standard Specifications of Roads & Bridges 2003. Stability values, at standard condition test, of samples containing 100% WCKD, 50%WCKD+50%C, and 50%WCKD+50%L are 11.9kN, 13.2kN, and 14.0kN respectively, while for controlled sample was 9.0kN. The Marshall stiffness values showed similar trends, for samples having 100% WCKD, 50%WCKD+50%C, and 50%WCKD+50%L giving 3.22kN/mm, 3.38kN/mm, 3.5kN/mm respectively but for controlled sample was 2.43 kN/mm. Same trends of results gained in ITST .The results showed the beneficial using of WCKD as filler that will conserve the environment and encourage the HMA producers to use this inexpensive material in their works.
This paper presents the experimental results of composite slabs under static and impact loading. Total of six specimens classified one specimen test under static loading and the remaining five were tests under impact dynamic loading with different parameters as type of connections and degree of interaction of composite slab. Low - velocity impact test was adopted by select the falling mass (4 kg) made from steel material and formed as ball shape without nose. The ball dropped freely from height of (2.4 m) and strikes the top of composite slab. The designed dimensions of specimens is (500×500×60 mm) as reinforced concrete slab that reinforced by mesh of (RBC) and the steel plate is (3 mm) in thickness. Deflection due to first crack is recorded, number of blows caused first crack and failure were counted. The test results showed that the welded stud connectors gives high strength capacity and resistance under static and impact dynamic loadings than other than type of connections, also, full interaction as degree of interaction is better than others